Hashemi Milani S A A, Tavangar R, Azadbeh M, Kahinpoor I, Sadeghi-Nasab H. Effect of NOCOLOK® Flux Dry-off Temperature on Mechanical Properties of Brazed Joint of Automotive Aluminum-Based Heat Exchangers. ISE. 2020; 10 (4) :3381-3393
URL: http://www.iust.ac.ir/ijae/article-1-521-en.html
sahand university of technology
Abstract:   (1023 Views)
Drying temperature of the flux at normal atmosphere has a crucial role in brazing quality in automotive aluminum-based heat exchangers. Over the course of this research, NOCOLOK® flux consists of two phases of K2AlF5.H2O and KAlF4 with melting point around 580 °C was used. A flux slurry was applied on the base metal, and dried at 220, 300 and 380 °C in air. Mechanical assessment revealed that when flux dried at 300 °C, the joint withstands maximum shear stress of 44 MPa with complete bonding. At 220 °C and 380 °C, joint shear stresses are 34 MPa, 30 MPa respectively. 380 °C dry-off temperature under nitrogen gas improved shear strength to 39 MPa. Taking dry-off temperature as 300 °C the amount of defective heat exchangers was reduced from 6% to 2% on a daily basis.
 
Full-Text [PDF 1058 kb]   (301 Downloads)    
Type of Study: Research | Subject: Manufacturing

Add your comments about this article : Your username or Email:
CAPTCHA

Send email to the article author


© 2018 All Rights Reserved | Automotive Science and Engineering

Designed & Developed by : Yektaweb