The Effect of lanthanum Substitution on the Ferroelectric and Piezoelectric Properties of (Pb0.88Sr0.12)(Zr0.54Ti0.44Sb0.02)O3 Ceramics

Goudarzi, 1-	Hossein; Baghshahi, Saeid; Tabarzadi, Reza

doi:10.22068/ijmse.4465

Volume 23, Issue 2 (June 2026 2026) IJMSE 2026, 23(2): 160-168 | Back to browse issues page

‎ 10.22068/ijmse.4465

Mendeley

Zotero

RefWorks

Goudarzi 1, Baghshahi S, Tabarzadi R. The Effect of lanthanum Substitution on the Ferroelectric and Piezoelectric Properties of (Pb0.88Sr0.12)(Zr0.54Ti0.44Sb0.02)O3 Ceramics. IJMSE 2026; 23 (2) :160-168
URL: http://ijmse.iust.ac.ir/article-1-4465-en.html

The Effect of lanthanum Substitution on the Ferroelectric and Piezoelectric Properties of (Pb0.88Sr0.12)(Zr0.54Ti0.44Sb0.02)O3 Ceramics

1- Hossein Goudarzi

, Saeid Baghshahi

, Reza Tabarzadi

Abstract: (1885 Views)

Piezoelectric ceramics based on lead zirconate titanate (PZT) with a composition of (Pb_0.88-3x/2Sr_0.12La_x)(Zr_0.54Ti_0.44Sb_0.02)O₃ where x=0.0, 0.005 and 0.01 were synthesized using conventional solid state sintering at 1280°C. The effect of lanthanum substitution on the microstructure, ferroelectric and piezoelectric properties of the samples was studied. The results showed that lanthanum substitution was beneficial for densification of the samples during sintering and the samples with 1.0 mole% lanthanum exhibited the maximum density of 7.34 g.cm^-3 when sintered at 1280°C. Moreover, the piezoelectric coefficient (d₃₃), relative dielectric constant (e_r), dielectric loss (tanδ), electromechanical coupling coefficient (k_p) and the Curie temperature (T_C) of the samples reached the optimal values of 635 pC/N, 3000, 0.018, 0.67 and 195°C respectively at 0.5 mole% lanthanum substitution. Furthermore, the bulk density (ρ) was 7.31 g.cm^-3 for the same sample. The results indicate that the lanthanum doped PSZTS ceramics can be hopefully used in applications such as pulsed transmitting transducers, high sensitivity receivers and actuators with large displacements.

Keywords: PSZTS, Lanthanum additive, ferroelectric and piezoelectric properties