Azadi M, Ferdosi M, Shahin H. The Effect of Different Heat Treatment Procedures on Duplex Stainless Steel Microstructures and Electrochemical Properties. IJMSE 2020; 17 (1) :91-101
URL: http://ijmse.iust.ac.ir/article-1-1459-en.html
Abstract:   (14577 Views)
In this paper, the effects of solutioning and various aging heat treatment processes on the microstructure, the hardness and electrochemical properties of a duplex stainless steel (DSS) were studied. The evaluation of the microstructure and phase compositions were carried out by the optical microscopy (OM) and the X-ray diffraction (XRD), respectively. Electrochemical behaviors of specimens were evaluated by both potentiodynamic polarization and electrochemical impedance spectra (EIS) tests at temperatures of 25 and 60 ºC. The obtained results showed that the solutioning heat treatment increased corrosion rates with respect to the blank specimen. The aging process at 490 ºC for 20 hrs increased the volume percent of the carbide phase to the highest value (25.1%) which resulted in an increase of the hardness value to 170 VHN. The specimen which was aged at 540 ºC for 10 hrs with the Cr7C3 size of 22.8 µm, exhibited the higher corrosion resistance at both temperatures of 25 and 60 ºC with respect to other aged specimens. In addition, the temperature of 60 ºC promoted the anodic reactions in 3.5 wt% NaCl solution which decreased impedance modulus values significantly. Consequently, the carbide size was more effective parameter than the carbide content in predicting electrochemical behaviors of such alloys. 
Full-Text [PDF 2880 kb]   (4118 Downloads)    
Type of Study: Research Paper | Subject: Surfe coating and corrosion

Add your comments about this article : Your username or Email:
CAPTCHA

Send email to the article author


Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2022 All Rights Reserved | Iranian Journal of Materials Science and Engineering

Designed & Developed by : Yektaweb