en Research Paper Research Paper <div style="text-align: justify;">In this research, the effect of initial microstructure and solution treatment on rollability and crystallographic texture of a Cu-Mn-Ni-Sn alloy has been investigated. The initial tests indicated that the rolling of the alloy at different temperature conditions is not possible due to formation of second phases. Herein to eliminate the segregated phases, according to DTA analysis, proper temperature for solution treatment was selected as 750&deg;C applied at different periods of time. The obtained results showed that after 15-hour solution treatment, the complete elimination of Sn, Mn, Ni, and Fe-rich phases can be achieved. Also, the peaks of XRD shifted to the higher angles indicating that the alloying elements are dissolved. Meanwhile, the intensity of the texture reduced and the dominant texture changed from Goss and Brass-texture to Copper-texture. Accordingly, the amount of maximum total reduction at the rolling process increased from 16.37 to 109.46 after solution treatment.</div> Microstructure,Texture,X-ray diffraction (XRD),rollability,Solution treatment 1 11 http://ijmse.iust.ac.ir/browse.php?a_code=A-10-2562-1&slc_lang=en&sid=1 Morteza Hadi 1800319475328460015105 1800319475328460015105 No Materials Engineering Group, Golpayegan College of Engineering, Isfahan University of Technology, 87717-67498, Golpayegan, Iran Omid Bayat obayat@hut.ac.ir 1800319475328460015106 1800319475328460015106 Yes Department of Metallurgy and Materials Engineering, Hamedan University of Technology, Hamedan,Iran Hadi Karimi 1800319475328460015107 1800319475328460015107 No Department of Materials Engineering, Malek-Ashtar University of Technology, 16788-15611, Iran Mohsen Sadeghi 1800319475328460015108 1800319475328460015108 No Department of Materials Engineering, Malek-Ashtar University of Technology, 16788-15611, Iran Taghi Isfahani 1800319475328460015109 1800319475328460015109 No Materials Engineering Group, Golpayegan College of Engineering, Isfahan University of Technology, 87717-67498, Golpayegan, Iran