JAVADPOUR J., Sakhaii K., Masihiyanpour A.a.,
Volume 1, Issue 4 (Jul 2004)
Abstract

Thin sheets of hydroxyapatite were fabricated by tape casting process. The non-aqueoustape casting formulation was optimized by adjusting the concentration of organic additivesspecially those of binder and plasticizer in the slurry. The optimized slurry was cast on a glasscarrier using a designed laboratory scale doctor blade. Following a binder removal stage, thetapes were sintered at different temperatures in air atmosphere. Heat treatment at 1250 °C led tothe formation of a dense microstructure as was evidenced by the scanning electron microscopy.
Baradari H., Amani Hamedani H., Karimi Khoygani S., Rezaei H.r., JAVADPOUR J., Sar Poulaki H.,
Volume 3, Issue 1 (Oct 2006)
Abstract

Ultrafine hydroxyapatite (HAp) powders with crystallite size in the range of 10-90 nm were synthesized by chemical precipitation process using Ca(OH)2 and H3PO4 solutions as starting materials. Molar ratio of Ca/P=1.68 was kept constant throughout the process and alkaline condition for the reaction was maintained using ammonium hydroxide. The role of raw material concentration on HAp crystallite size and morphology were investigated using X-ray diffraction (XRD) and scanning electron microscope (SEM) techniques. The results revealed that variations in crystallite size and morphology of synthesized HAp are strongly affected by the concentration of acid solution. To study the sintering behavior of HAp particles, the powders were pressed at 200 MPa using a uniaxial press. Sintering experiments were carried out at temperatures of 1100, 1250 and 1300°C with various soaking times at maximum temperatures. XRD was also used in determining thephases present after sintering process. The results indicated the decomposition of HAp into a-tricalcium phosphate (TCP) and b-TCP phases at 1300°C. The microstructure of the sintered HAp ceramics was characterized by SEM.

Page 1 from 1     

© 2019 All Rights Reserved | Iranian Journal of Materials Science and Engineering

Designed & Developed by : Yektaweb