Mirzakouchakshirazi H, Eivani A, Kheirandish S. EFFECT OF POST-DEFORMATION ANNEALING TREATMENT ON INTERFACE PROPERTIES AND SHEAR BOND STRENGTH OF Al-Cu BIMETALLIC RODS PRODUCED BY EQUAL CHANNEL ANGULAR PRESSING. IJMSE 2017; 14 (4) :25-34
URL: http://ijmse.iust.ac.ir/article-1-997-en.html
Abstract:   (19198 Views)
Effects of annealing treatment after equal channel angular pressing (ECAP) on the interface properties and shear bond strength of Al/Cu bimetallic rods were investigated. For the as-deformed samples, the one with two passes of ECAP indicated higher shear bond strength. Formation of a layer of intermetallic compounds after annealing treatment is confirmed. In general, by increasing annealing temperature, thickness of intermetallic compounds at the interface increases. Shear bond strength was initially reduced by annealing at 200, 250 and 300 ͦ C and increased at 350 ͦ C. With further increase in annealing temperature to 400 ͦ C, shear bond strength slightly decreased which is correlated to the increased thickness of the intermetallic compounds.
Full-Text [PDF 1427 kb]   (7270 Downloads)    

Add your comments about this article : Your username or Email:
CAPTCHA

Send email to the article author


Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2022 All Rights Reserved | Iranian Journal of Materials Science and Engineering

Designed & Developed by : Yektaweb