A. R. Abbasian, M. R. Rahimipour, Z. Hamnabard. INITIAL SINTERING KINETICS OF LITHIUM META TITANATE AT CONSTANT RATES OF HEATING. IJMSE 2013; 10 (3) :44-53
URL: http://ijmse.iust.ac.ir/article-1-573-en.html
Abstract:   (19502 Views)
In order to evaluate the sintering behavior of lithium meta titanate (Li2TiO3) powder, the shrinkage of powder compact was measured under constant rates of heating. Densification curves for Li2TiO3 have been constructed with the help of shrinkage powder measured at different heating rates. The activation energy at the initial stage of sintering was determined by analyzing the densification curves and the value of Q=377 kJ/mol was obtained. The diffusion mechanism at the initial sintering stage was determined by the analytical method applied to the constant rates of heating data. This analysis exhibited that the dominant mechanism for initial sintering stage of Li2TiO3 is volume diffusion from grain boundary and surfaces.
Full-Text [PDF 1006 kb]   (5597 Downloads)    
Type of Study: Research Paper |

Add your comments about this article : Your username or Email:
CAPTCHA

Send email to the article author


Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2022 All Rights Reserved | Iranian Journal of Materials Science and Engineering

Designed & Developed by : Yektaweb