Showing 3 results for Strength Concrete
Mazloom M., Ramezanian Pour A.a.,
Volume 2, Issue 1 (3-2004)
Abstract
This paper presents the long-term deformations of reinforced high-strength concrete columns subjected to constant sustained axial forces. The objective of the study was to investigate the effects of binder systems containing different levels of silica fume on time-dependent behaviour of high-strength concrete columns. The experimental part of the work focused on concrete mixes having a fixed water/binder ratio of 0.35 and a constant total binder content of 500 kg/m3. The percentages of silica fume that replaced cement in this research were: 0%, 6%, 8%, 10% and 15%. The mechanical properties evaluated in the laboratory were: compressive strength secant modulus of elasticity strain due to creep and shrinkage. The theoretical part of the work is about stress redistribution between concrete and steel reinforcement as a result of time-dependent behaviour of concrete. The technique used for including creep in the analysis of reinforced concrete columns was age-adjusted effective modulus method. The results of this research indicate that as the proportion of silica fume increased, the short-term mechanical properties of concrete such as 28-day compressive strength and secant modulus improved. Also the percentages of silica fume replacement did not have a significant influence on total shrinkage however, the autogenous shrinkage of concrete increased as the amount of silica fume increased. Moreover, the basic creep of concrete decreased at higher silica fume replacement levels. Drying creep (total creep - basic creep) was negligible in this investigation. The results of the theoretical part of this researchindicate that as the proportion of silica fume increased, the gradual transfer of load from the concrete to the reinforcement decreased and also the effect of steel bars in lowering the concrete deformation reduced. Moreover, the total strain of concrete columns decreased at higher silicafume replacement levels.
Khaloo R., Sharifian M.,
Volume 3, Issue 3 (9-2005)
Abstract
Results of an experimental investigation performed to evaluate the effect of various concrete strength levels on behavior of lightweight concrete (LWC) under pure torsion are reported.The principle variable of the testing program was compressive strength of concrete (�'c) which ranged between 6.9 and 81.4 MPa. Ten mixture proportions were utilized for LWC of 1500 to 2050 kg/m3 unit weight. In total, sixty four (thirty two pairs) rectangular specimens with 100x 200 mm cross-section were tested. Ultimate torsion strength of LWC increases as uniaxial compressive strength increases however the increase rate reduces for high levels of concrete strengths. The test results are compared with predictions of elastic and plastic theories for torsion and the ACI Code. The Code underestimates the cracking torque of LWC under pure torsion. A regression equation incorporating test results is higher than the ACI equation prediction by a factor of 1.12.
P. Ramadoss,
Volume 12, Issue 1 (3-2014)
Abstract
Abstract: This paper presents the influence of adding steel fibers and incorporation of silica fume on the mechanical properties of high-strength concrete. The variables investigated were steel fiber volume fraction (0 to 1.5%), silica fume replacement (5, 10 and 15%) and water-to-binder ratio (0.25, 0.30, 0.35 and 0.40). The influence of fiber content in terms of fiber reinforcing index on the compressive and splitting tensile strengths of high-strength steel fiber reinforce concrete (HSFRC) is presented. The use of silica fume increased both the compressive and splitting tensile strengths of concrete at 28 days. On the other hand, the addition of crimped steel fiber into high-strength concrete improves splitting tensile strength significantly. Based on the test data, using regression analysis, empirical expression to predict 28-day tensile strength of HSFRC in terms of fiber reinforcing index was developed and the absolute variation and integral absolute error (IAE) obtained was 3.1% and 3.3, respectively. The relationship between splitting tensile and compressive strength of SFRC was reported with regression coefficient (r) = 0.9. The experimental values of previous researchers were compared with the values predicted by the model and found to predict the values quite accurately.