Nojehdehyan H., Moztar Zadeh F., Mir Zadeh Hamid, Hesaraki S., Keyanpour-Rad M.,
Volume 2, Issue 2 (Jan 2005)
Abstract

The effect of addition of NaHF2 on the cement setting and the set mass has been studied as an initial step to determine how fluoride influences the characteristics of a calcium phosphate cement, consisting of tetracalcium phosphate [TTCP:Ca4 (PO4)2O] and dicalcium phosphate dihydrate [DCPD:CaHPO4.2H2O].NaHF2 [0-10% wt% of powder phase] has been dissolved in double distilled water and used as the liquid phase of the apatite cement (AC). Powder X-ray diffraction analysis and FTIR measurements revealed that fluoride was necessary in promoting the formation of the apatite phase. The setting time was decreased significantly by the addition of NaHF2from 0% to 6%, but increased resulted in the AC (8-10%). The set AC (2%) has the highest compressive strength and the lowest porosity.The dissolution rate of set AC in weak acid, pH 5.5, was decreased with the amount of added NaHF2 from 0% to 6% but increased in the set AC 8-10%.The formation of fluoroapatite in AC (6%) was provided the low solubility and good acid resistance which is necessary for dental application.SEM observation showed needle-like apatite crystal growth over particulate matrix surface, however the amount of non-reactive TTCP or DCPD particles decreased by the addition of NaHF2. The Ca/P ratio, which was determined by EDAX, increased significantly with the addition of NaHF2.
M. Keyanpour-Rad, S. Keyanpour-Rad,
Volume 5, Issue 3 (Summer 2008 2008)
Abstract

Abstract: A novel dust free alginate impression material was formulated and prepared, comprising an alginate polyvinylpyrrolidone and tetraflouroethylene resins, a mixture of liquid paraffin and dimethylpolysiloxane oil as the dust generation controlling agents and processed diatomaceous earth filler which was obtained from Iranian ore. No dusting was detected during the mixing of the powder and the conventional properties of the impression material, like working and setting times and compressive strength were in the range of the required specifications for alginate dental impressions. The compressive strength was measured to be 2.6 times of the minimum requirement for such fast setting impressions.
F. Torknik, M. Keyanpour-Rad, A. Maghsoudipour, G. M. Choi,
Volume 13, Issue 1 (March 2016)
Abstract

In order to further enhance the Ni/Ce 0.8Gd0.2O2-δ (Ni/GDC20) cermet anodic performance for low temperature solid oxide fuel cell (LT-SOFC), a study was conducted on the nanostructuring of NiO/GDC composite by only once wet-infiltration of rhodium chloride precursor. By using electrochemical impedance spectroscopy (EIS) analysis, the effect of only one drop of Rh-infiltrating solution on the anodic polarization resistance was examined using symmetric Ni–GDC20|GDC20|Pt electrolyte-supported cell at 400-600 °C. Nanostructural evolution before and after H 2 reduction at 600 °C and also after anodic performance test was investigated by atomic force microscopy (AFM), field emission scanning electron microscopy (FE-SEM), and transmission electron microscopy (TEM) techniques in comparison to the anode itself. Despite the fine distribution of Rh-infiltrated nanoparticles having average particle size of 11.7 nm, the results showed ineffectiveness and inability of the Rh nanoparticles to succeed in decreasing of anodic polarization resistance for H 2 oxidation reaction in LT-SOFC.