titanium sheets in pure molten aluminum at 750

and X-Ray Diffraction Analysis results, TiAl

intermetallic layer thickness increases slowly at primary stages. After that an enhanced growth rate occurs due to layer

cracking and disruption. Presumably, reaction starts with solving titanium into the molten aluminum causing in

titanium super saturation and TiAl

intermetallic layer which consequently leads to TiAl

energy of intermetallic layer formation and growth was developed by measuring titanium thickness decreases.

In this work, kinetics of intermetallic compounds formation in Al-Ti system was studied by immersingoC, 850 oC and 950 oC. According to Scanning Electron Microscopy3 is the only phase can form at the interface. Observations revealed that3 formation. At this stage, growth may be controlled by aluminum diffusion through3 formation at the interface of Ti-TiAl3. Furthermore, activation